White Fused Alumina

Contact us
product description

White Corundum Density

  Density is Divided Into Two, One Is The Accumulation Density, The Second Is True Density.

Accumulation Density

  1.53~1.99g/cm3, The Accumulation Density Of Abrasive Is Related To The Particle Size Of Abrasive And The Grain Shape Of the Constituent Varieties Generally Speaking, The Bulk Density Of Coarse Abrasive Is Higher Than That Of Fine Abrasive, And The Bulk Density Of Mixed Abrasive Is Higher Than That of single Abrasive.

True density

  3.95~4.0g/cm3, The true Density of Abrasive refers to the Quality of Abrasive contained in unit Volume (excluding the volume of open pores).

Basic Particle Size

  45%~55%. The basic particle size is an important index to ensure the grinding effect. It should be controlled properly during production, But the production Speed may be slowed down.

Product advantages

  1, Does not affect the color of the Workpiece

  2. Sandblasting can be used in the process where iron residue is strictly prohibited

  3, Micro powder level is very suitable for wet sandblasting and polishing operations

  4. Fast processing speed and high quality;

  5, The content of iron oxide is very low suitable for strictly prohibited iron residue sandblasting operation

  6. Remove impurities by pickling

Physical properties

  Crystal:Trigonal system

  True density: 3.90 g/cm3

  Bulk density: 3.60g/cm3

  Hardness 1Mr Spectral hardness 2000 - 2200 Kg/mm2

  2 Mohs hardness 10.0

  Color: White

  Melting point: 2250 C

  Maximum service temperature: 1900 C

  Specific heat (Cal/g. C): 0.26 (20 - 90 C)

  Thermal conductivity: Room temperature is 900 C (Cal/cm3. sec. C)

  Refractive index: e=1.760 w=1.768(Na line)

  The resistivity: 30 C 300 C 900 C 1600 C(cm) 10、16、10、13、10、5、10、4

  Linear expansion coefficient: (7 - 9)*10^-6/K (0 - 1600 C)

  Chemical properties: Both sexes 1 .React with acid and slightly corrode in aqua regia and hydrofluoric acid 2. React with alkali only slightly with hot alkali solution

The physical and chemical indicators

Use Specifications Chemical composition%      
    Al2O3 Na2O Fe2O3 SiO2
Abrasives 12#-80# 99.28 ≤0.4 ≤0.03 ≤0.03
  90#—150# 99.21 ≤0.4 ≤0.03 ≤0.05
  180#—240# 99.18 ≤0.4 ≤0.03 ≤0.03
Micro powder W63-W1 99.2 ≤0.4 ≤0.03 ≤0.05
Refractory Period of sand Fine powder 0-1mm ≥99 ≤0.4 ≤0.1 ≤0.02
8-12mm ≥99.18 ≤0.4 ≤0.06 ≤0.05